OPTOLINQ TMC-2100 | Transparent Mold Compound
Harmonization Code : 3907.30.00.85 | Polyacetals, other polyethers and epoxide resins, in primary forms; polycarbonates, alkyd resins, polyallyl esters and other polyesters, in primary forms : Epoxide resins : Other
Main features
- Exceptional moldability with long spiral flow
- Low moisture absorption
- Excellent reliability
Product Description
OPTOLINQ TMC-2100 is an optically clear epoxy molding compound specifically designed for the encapsulation of optoelectronic devices. With its high spiral flow, it ensures precise and intricate molding.
OPTOLINQ TMC-2100 offers excellent moisture resistance, maintaining performance even in high temperature and humidity conditions. TMC-2100 stands out with its superior moldability and reliability, ensuring good quality and precision in optoelectronic device molding.
OPTOLINQTM TMC-2100IR is an optically clear epoxy molding compound specifically designed for the encapsulation of applications that require infrared transparency. With its large spiral flow, it ensures precise and intricate molding. TMC-2100IR exhibits a low moisture absorption and high moisture resistance maintaining performance in high temperature and humidity conditions. Contact us for custom sizes or other specific requirements.
Key Features
- High IR Transparency: Ensures superior infrared light transmission for optimal device performance.
- Low Moisture Absorption & Excellent Moisture Resistance: Effectively prevents moisture ingress, safeguarding long-term reliability.
- Reliable Under Harsh Conditions: Maintains consistent performance in environments with elevated temperature and humidity.
- High Adhesion & Low Stress: Provides strong, durable bonding with minimal internal stress, reducing risk of delamination or cracking.
Typical Applications
- Low-Power LED & Emitters
- Pulse Oximeter Sensors
- Ambient Light Sensors
- IR and Near-IR Sensors
- Data transmission and industrial fibers.
Versions Available
- Standard Low stress optical molding compound - TMC-2100
- Enhanced self-release, visible-pass with NIR filtering (>1100 nm) - TMC-2100H
- Superior IR optical transparency - TMC-2100IR
Alternative to: XX-8524 Series, XX-824H, XX-330H.
TMC-2100
Unlike other products we offer, the products listed on this page cannot currently be ordered directly from the website.
Shipping in 2 weeks
Shipping in 2 weeks
Shipping in 2 weeksPackaging
TDS, SDS & Technical Documents
- MSDS_OPTOLINQ TMC-2100
- TDS_OPTOLINQ TMC-2100
Technical Specifications
General Properties
Thermal Properties
Curing Conditions
Physical Properties
Additional Information
| Property | Value | Unit |
|---|---|---|
| Specific gravity | 1.20–1.25 | – |
| Hardness at 25 °C | 80 | Shore D |
| Gel time at 150 °C | 35–60 | s |
| Spiral flow at 150 °C | 80–180 | cm |
| Mold shrinkage | 1.5 | % |
| Glass transition temperature by TMA | 120±10 | °C |
| Coefficient of thermal expansion, α1 | 60–100 | ppm/K |
| Coefficient of thermal expansion, α2 | 170–210 | ppm/K |
| Flexural strength | 110 | MPa |
| Flexural modulus | 2.6–3.4 | GPa |
| Transmittance at 400 nm | >85 | % |
OPTOLINQ TMC-2100 | Optically Clear Molding Compound
TMC-2100 is developed to exhibit robust optical performance, TMC-2100IR a high IR transparent version designed for applications operating above the visible light spectrum.
OPTOLINQ TMC-2100IR | Optically Clear Molding Compound
TMC-2100IR boasts its blended chemistry system to improve IR transparency through refractive index matching and IR-transparent fillers. The transmittance shown is measured at 2 mm thick sample and will exhibit higher transmittance at a thinner samples and packages.
Inspected specimens are 1 mm thick sample cured in mold for 4 minutes at 150°C and post cured for 4 hours at 150°C. 
Inspected specimens are 2 mm thick sample cured in mold for 4 minutes at 150°C and post cured for 4 hours at 150°C.
Featured BMC-4200H Variants: CAPLINQ Product Offerings
OPTOLINQ BMC for Filter Applications
Looking to enhance optical precision and durability in your filter-integrated optoelectronic devices? This short presentation introduces OPTOLINQ’s clear molding compounds specifically designed for high-performance filter applications.
Featuring BMC-4200H, a versatile formulation available in six onset wavelengths (700, 720, 750, 820, 840, and 870 nm), our clear compounds offer exceptional light control, environmental resistance, and long-term optical clarity.
Whether you're fine-tuning signal filtering, improving IR sensitivity, or ensuring high transmission and structural stability, OPTOLINQ compounds are built to perform—clear, consistent, and reliable.
Got questions or need help selecting the right optical grade for your filter applications? Reach out to us!
Contact Us →
Directions Before Use
- Thaw TMC-2100 to room temperature (20±5℃, 40±15%RH) at least 24 hours before use. Do not open the bag to avoid moisture contamination.
- Slowly preheat the molding compound using standard RF equipment.
Recently viewed products
Humiseal 1A27LU | Urethane Conformal Coating
- Isocyanate-free
- Single-component
- UV fluorescent
PIT0.5N-DCD | 0.5 mil Die Cut Polyimide (Kapton) Film| Single Sided Discs
- 0.5 mil polyimide film
- No adhesive
- Die cut discs
ALPHA PoP707 Lead-Free No-Clean Solder Paste
- Fine particle dispersion (<10 µm)
- ROL0 per IPC J‑STD‑004
- Outstanding SIR performance
HumiSeal Thinner 999
- Optimized viscosity control
- RoHS compliant
- High-purity solvent blend
Aculon Nanoproof 3-02
- 2% Fluoroacrylate Solids
- 0-2 - 2 um Thickness
- 3M Novec 1700, 1902 replacement
FM-0421 | Reactive PDMS - Monoterminal Hydroxy
- Mono terminal
- 5,000 g/mol | 70 mPas
- Hydroxy functional group
ALPHA SC-7525 Cleaner
- IPA alternative
- High solvency
- Suitable for manual & immersive methods
ABchimie 6025UV LED Soft Thixotropic Resin
- One component
- UV LED Cure
- Shock Absorbing
3M™ Scotch-Weld™ Epoxy Adhesive 7240 FR
- Long open time for large surface application
- Non-sag properties
- Contains glass beads for thickness control